国际口腔医学杂志 ›› 2013, Vol. 40 ›› Issue (4): 436-439.doi: 10.7518/gjkq.2013.04.005

• 论著 • 上一篇    下一篇

长期水储存对玻璃陶瓷与牙本质间树脂粘接界面的影响

李励芸 魏文佳 孟翔峰   

  1. 南京大学口腔医学院•南京市口腔医院修复科 南京 210008
  • 收稿日期:2012-12-28 修回日期:2013-04-21 出版日期:2013-07-01 发布日期:2013-07-01
  • 通讯作者: 孟翔峰, Tel: 025-83620261
  • 作者简介:李励芸(1987—), 女, 安徽人, 硕士
  • 基金资助:

    南京市医学科技发展基金资助项目(ZKX09035)

The effect of long-term water storage on the resin adhesive interface between dentine and glass ceramic

Li Liyun, Wei Wenjia, Meng Xiangfeng.   

  1. Dept. of Prosthodontics, Nanjing Stomatological Hospital, School of Stomatology, Nanjing University, Nanjing 210008, China
  • Received:2012-12-28 Revised:2013-04-21 Online:2013-07-01 Published:2013-07-01

摘要:

目的 分析长期水储存条件下玻璃陶瓷与牙本质间树脂粘接界面劣化的薄弱点。方法 选择完整健康的第三磨牙获得牙本质表面, 表面分别接受酸蚀-冲洗型树脂粘接系统One-step Plus+Duolinks(OD); 自酸蚀型树脂粘接系统ED -Primer +Panavia F(EP)、Multilink Primer +Multilink Automix(MM)、J -100P Primer +J -100PIvory(JJ); 自粘接型树脂水门汀Relyx Unicem(RU)处理后, 与表面经硅烷偶联剂预处理的玻璃陶瓷块(ProCAD)进行粘接, 经光照射后将瓷块切割成粘接面积约为0.9 mm×0.9 mm的拉伸试件, 经过18个月水储存后, 接受拉伸测试。结果 拉伸试件断裂形式分析显示, 单纯的陶瓷界面断裂形式所占比例: OD组64%, EP组57%, MM组79%, JJ组36%,RU组39%, 而单纯的牙本质界面断裂形式所占比例: OD组0%, EP组14%, MM组4%, JJ组7%、RU组14%, 其余为涉及陶瓷界面的混合断裂形式。粘接强度结果显示, OD组(12.98±5.86)MPa高于MM组(9.32±2.87)MPa, 其差异具有统计学意义(P<0.05), 但其余3组与OD组和MM组的差异无统计学意义(P>0.05)。结论 在长期水储存下, 树脂与玻璃陶瓷粘接界面比牙本质与树脂粘接界面更容易出现老化, 酸蚀-冲洗型树脂粘接系统能够获得更稳定的牙本质树脂粘接界面。

关键词: 牙本质, 玻璃陶瓷, 树脂水门汀, 水储存, 粘接界面

Abstract:

Objective To analyze the weak point of multiple adhesive interfaces between dentine and glass ceramic through resin cement under long-term water storage. Methods The flat dentin surfaces of 15 intact human third molars and 15 pieces of glass ceramic(ProCAD) pretreated by silane coupler were prepared. The teeth were divided into 5 groups randomly, were bonded with ceramic through etch -rinse type resin adhesive system One-step Plus +Duolinks(OD); self-etch type resin adhesive system ED-Prime+Panavia F(EP), Multilink Primer+Multilink Automix(MM), and J-100P primer+J-100P Ivory(JJ); self-adhesive type resin cement Relyx Unicem(RU). The bonded teeth were sectioned to obtain bar -shaped intact specimens with about 0.9 mm× 0.9 mm bond area. Specimens were kept in distilled water for 18 months, and received mirco -tensile test. Results The count of fracture mode showed that ceramic interface fracture were 64% in Group OD, 57% in Group EP, 79% in Group MM, 36% in Group JJ, 39% in Group RU, while dentine interface fracture were 0% in Group OD, 14% in Group EP, 4% in Group MM, 7% in Group JJ, 14% in Group RU, and the others were the mixture fracture which all included the part of ceramic interface fracture. The bond strengths of Group OD(12.98±5.86)MPa was greater than those of Group MM(9.32±2.87)MPa(P<0.05), and the bond strength of Group EP, Group JJ and RU were not significantly different from Group OD and Group MM(P >0.05). Conclusion The interface of resin cements and ceramics is more susceptible from water than that of resin and dentine, etch-rinse type resin bond system could obtain more stable adhesive interface.

Key words: dentine, glass ceramic, resin cement, water storage, adhesive interface

[1] 雷彬,陈柯. 牙本质发育不良Ⅰ型及其分型治疗[J]. 国际口腔医学杂志, 2022, 49(3): 332-336.
[2] 李嫣斐,张新春. 牙本质作为骨修复材料的研究进展[J]. 国际口腔医学杂志, 2022, 49(2): 197-203.
[3] 丁景瑜,田子璐,王惠敏,朱轩言,杨宇斌,朱松. 即刻牙本质封闭的研究进展[J]. 国际口腔医学杂志, 2022, 49(1): 121-124.
[4] 章善,沈树平,张舫,杨卫东. Er: YAG激光光子激活光声流技术对根管壁牙本质失水状况及牙根抗压强度的影响[J]. 国际口腔医学杂志, 2022, 49(1): 55-59.
[5] 何蓉,刘学军,周宇琨. 光子引导的光声流效应在根管荡洗中应用的系统评价[J]. 国际口腔医学杂志, 2021, 48(6): 644-655.
[6] 赵彬彬,仲维剑,马国武. 牙本质作为骨移植材料的研究进展[J]. 国际口腔医学杂志, 2021, 48(1): 82-89.
[7] 刘恩言,李明云. 茶多酚类化合物在牙本质粘接中应用的研究进展[J]. 国际口腔医学杂志, 2020, 47(6): 732-738.
[8] 张凯莹,房付春,吴补领. 非编码RNA在牙源性干细胞成牙本质向分化中作用的研究进展[J]. 国际口腔医学杂志, 2019, 46(5): 540-545.
[9] 秦娇娇,焦珊,王成坤. Er:YAG和Nd:YAG激光对牙本质与瓷修复体粘接面粘接强度影响的研究进展[J]. 国际口腔医学杂志, 2019, 46(3): 361-366.
[10] 谭欣,于海洋. 模拟髓腔压力在牙本质粘接强度研究中的应用[J]. 国际口腔医学杂志, 2018, 45(6): 723-727.
[11] 陈燕活, 安少锋, 高燕. 硅酸钙类盖髓剂生物学性能的研究进展[J]. 国际口腔医学杂志, 2018, 45(4): 459-464.
[12] 廖文婷, 李彦. 半胱氨酸组织蛋白酶对牙本质粘接耐久性的影响[J]. 国际口腔医学杂志, 2017, 44(3): 340-343.
[13] 张雅蓉, 刘洋, 张玲, 于海洋. 不同切端设计的上前牙瓷贴面受载能力的定量研究[J]. 国际口腔医学杂志, 2017, 44(3): 301-303.
[14] 武芳艳,李明菲,孟翔峰. 铸瓷全冠修复体树脂粘接效果的3年临床评估[J]. 国际口腔医学杂志, 2016, 43(6): 658-660.
[15] 陈尽欢,孙建勋,陈新梅. 转化生长因子-β超家族成员在牙本质发生发育中的作用[J]. 国际口腔医学杂志, 2016, 43(4): 477-481.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] 张京剧. 青年期至中年期颅面复合体变化的头影测量研究[J]. 国际口腔医学杂志, 1999, 26(06): .
[2] 刘玲. 镍铬合金中铍对可铸造性和陶瓷金属结合力的影响[J]. 国际口腔医学杂志, 1999, 26(06): .
[3] 王昆润. 在种植体上制作固定义齿以后下颌骨密度的动态变化[J]. 国际口腔医学杂志, 1999, 26(06): .
[4] 王昆润. 重型颌面部炎症死亡和康复病例的实验室检查指标比较[J]. 国际口腔医学杂志, 1999, 26(06): .
[5] 逄键梁. 两例外胚层发育不良儿童骨内植入种植体后牙槽骨生长情况[J]. 国际口腔医学杂志, 1999, 26(05): .
[6] 温秀杰. 氟化物对牙本质脱矿抑制作用的体外实验研究[J]. 国际口腔医学杂志, 1999, 26(05): .
[7] 杨春惠. 耳颞神经在颞颌关节周围的分布[J]. 国际口腔医学杂志, 1999, 26(04): .
[8] 王昆润. 牙周炎加重期应选用何种抗生素[J]. 国际口腔医学杂志, 1999, 26(04): .
[9] 杨儒壮 孙宏晨 欧阳喈. 纳米级高分子支架材料在组织工程中的研究进展[J]. 国际口腔医学杂志, 2004, 31(02): 126 -128 .
[10] 严超然,李龙江. 肿瘤靶向药物载体系统的研究进展[J]. 国际口腔医学杂志, 2008, 35(S1): .