Inter J Stomatol ›› 2013, Vol. 40 ›› Issue (3): 305-308.doi: 10.7518/gjkq.2013.03.007

Previous Articles     Next Articles

Study of bonding property among 3 kinds of resin-reinforced glass ionomer and zirconia ceramics

Lin Yihua1, Song Xiaomeng2, Zhang Wei3   

  1. 1. Dept. of Stomatology, The Chinese Medicine Hospital of Xiangshan in Zhejiang Province, Ningbo 315700, China; 2. Dept. of Oral and Maxillofacial Surgery, Stomatological Hospital of Jiangsu Province, Institute of Stomatology of Nanjing Medical University, Nanjing 210029, China; 3. Dept. of Oral Special Consultation, Stomatological Hospital of Jiangsu Province, Institute of Stomatology of Nanjing Medical University, Nanjing 210029, China
  • Received:2012-07-23 Revised:2013-01-29 Online:2013-05-01 Published:2013-05-01

Abstract:

Objective To study the bonding efficiency of zirconia ceramics with 3 kinds of resin-reinforced glass ionomer. Methods Blocks of sintered zirconia ceramics were cut and randomly divided into 3 groups with 20 slices each. They were treated with sandblasting and bonded with 3 kinds of resin-reinforced glass ionomer respectively. After preserved in distilled-water for 24 hours and aged by thermocycling 5 000 times, the shear bond strength of these specimens was tested and data were analyzed by SPSS 11.5 system for windows. The bonding face was observed by scanning electron microscope. Results The shear bond strength of the ceramic and 3 kinds of resin-reinforced glass ionomer was (15.1±3.2), (16.1±4.0), (18.6±3.4)MPa(after preserved in distilled-water for 24 hours) respectively, and decreased greatly to (5.1±2.1), (7.5±2.9), (8.7±2.6)MPa(after thermocycling 5 000 times). There was obvious statistical difference before and after thermocycling(P<0.05). Conclusion Resin-reinforced glass ionomer can get good initial bond strength with zirconia ceramics, but the bonding durability is poor.

Key words: resin-reinforced glass ionomer, zirconia ceramics, shear bond strength, bonding durability


TrendMD: 
[1] Li Min,Hua Chengge,Jiang Li. Research progress on new technology for improving adhesion properties of zirconia ceramics [J]. Int J Stomatol, 2021, 48(4): 485-490.
[2] Ding Hong, Chen Jifen, Wu Jianyong. Influence of different adhesive materials on the shear bond strength of metal brackets to porcelain surface [J]. Inter J Stomatol, 2017, 44(4): 430-432.
[3] Liao Wenting, Li Yan.. Influence of cysteine cathepsins on dentin bonding durability [J]. Inter J Stomatol, 2017, 44(3): 340-343.
[4] Yao Chenmin, Zhou Liqun, Huang Cui.. Selection of tooth-colored restorative material for worn anterior teeth [J]. Inter J Stomatol, 2017, 44(3): 363-367.
[5] Zhao Zheshan, Qiu Rongmin, Huang Hua. Research progress on orthodontic adhesive [J]. Inter J Stomatol, 2016, 43(4): 417-420.
[6] Sun Qiurong, Mai Sui. Research progress on the permeability of resin-dentine bonds and bonding durability [J]. Inter J Stomatol, 2016, 43(3): 338-342.
[7] Zhong Qun, Shen Qingyi, Wu Xueying, Li Guoqiang.. Shear bond strengths of different types of adhesive resin agents to glass infiltrated alumina oxide ceramic [J]. Inter J Stomatol, 2012, 39(1): 16-19.
[8] XIA Song-xin, LIN Zhengmei.. Research progress of the bonding durability of resin-based root canal sealers [J]. Inter J Stomatol, 2010, 37(6): 681-684.
[9] JIN En- long, JIAO Yan- jun. Application of Zir conia Cer amics in Dental Use [J]. Inter J Stomatol, 2007, 34(01): 62-62~64.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[2] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[3] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[4] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[5] . [J]. Foreign Med Sci: Stomatol, 1999, 26(05): .
[6] . [J]. Foreign Med Sci: Stomatol, 1999, 26(05): .
[7] . [J]. Foreign Med Sci: Stomatol, 1999, 26(04): .
[8] . [J]. Foreign Med Sci: Stomatol, 1999, 26(04): .
[9] . [J]. Foreign Med Sci: Stomatol, 2004, 31(02): 126 -128 .
[10] . [J]. Inter J Stomatol, 2008, 35(S1): .