镍铬和含钛镍铬烤瓷合金的耐腐蚀性能研究

摘要/Abstract

摘要： 目的评价2 种镍铬和1 种含钛镍铬烤瓷合金试件在人工唾液中的耐腐蚀性能。方法采用电化学极化曲线法测定2 种镍铬和1 种含钛镍铬烤瓷合金试件的自腐蚀电流密度（Icorr ）、极化电阻（Rp）、自腐蚀电位（Ecorr ），并得出3 种合金的极化曲线。应用场发射扫描电子显微镜（FSEM）观察实验前后试件表面形貌变化，并对数据进行单因素方差分析。结果 Bellabond 镍铬烤瓷合金的Icorr 低于Neotitan 含钛镍铬烤瓷合金（P<0.05）及粤海镍铬烤瓷合金（P>0.05）；粤海镍铬烤瓷合金Icorr 低于Neotitan 含钛镍铬烤瓷合金（P＞0.05）。Bellabond 镍铬烤瓷合金的Rp 明显高于粤海镍铬烤瓷合金（P<0.05）及Neotitan 含钛镍铬烤瓷合金（P<0.05）；粤海镍铬烤瓷合金试件的Rp 高于Neotitan 含钛镍铬烤瓷合金（P>0.05）。Bellabond 镍铬烤瓷合金的Ecorr 低于粤海镍铬烤瓷合金（P>0.05）及Neotitan 含钛镍铬烤瓷合金（P>0.05）；Neotitan 含钛镍铬烤瓷合金的Ecorr 高于粤海镍铬烤瓷合金（P>0.05）。FSEM 显示，Bellabond 镍铬烤瓷合金表面腐蚀较粤海镍铬烤瓷合金和Neotitan 含钛镍铬烤瓷合金轻微。结论 Bellabond 镍铬烤瓷合金的耐腐蚀性较粤海镍铬烤瓷合金和Neotitan 含钛镍铬烤瓷合金优良，Neotitan含钛镍铬烤瓷合金耐腐蚀性与粤海镍铬烤瓷合金无明显差异。

关键词: 牙科合金

Abstract: Objective To evaluate the corrosion resistance of two kinds of Ni-Cr alloy and Neotitan Ni-Cr-Ti alloy. Methods Electrochemical methods were used to measure the self-corrosion current density（Icorr ） , polarization resistance（Rp） and self -corrosion potential（Ecorr ） of three alloys. And the polarization curves of the three alloys were recorded at the same time. Field scanning electron microscope（FSEM） was used to observe the corrosion in the surface of the three alloys. One-way ANOVA with SPSS 11.0 software package was used for statistical analysis. Results The Icorr of Bellabond Ni-Cr alloy was lower than that of Neotitan Ni -Cr-Ti alloy（P<0.05）and Yuehai Ni-Cr alloy（P>0.05）. The Icorr of Yuehai Ni-Cr alloy was lower than that of Neotitan Ni-Cr-Ti alloy
（P＞0.05）. The Rp of Bellabond Ni-Cr alloy was higher than that of Yuehai Ni-Cr alloy（P<0.05） and Neotitan Ni-Cr-Ti alloy（P<0.05）. The Rp of Yuehai Ni-Cr alloy was higher than that of Neotitan Ni-Cr-Ti alloy（P>0.05）. The Ecorr of Bellabond Ni-Cr alloy was lower than that of Yuehai Ni-Cr alloy（P>0.05） and Neotitan Ni-Cr-Ti alloy（P>0.05）. The Ecorr of Neotitan Ni-Cr-Ti alloy was higher than that of Yuehai Ni-Cr alloy（P>0.05）. FSEM showed that the corrosion in the surface of Bellabond Ni-Cr alloy was slighter than that of Yuehai Ni-Cr alloy
and Neotitan Ni-Cr-Ti alloy. Conclusion The corrosion resistance of Bellabond Ni-Cr alloy is better than that of Yuehai Ni-Cr and Neotitan Ni-Cr-Ti alloy. The corrosion resistance of Neotitan Ni-Cr-Ti alloy had no difference compared with that of Yuehai Ni-Cr alloy.

孙平，冯剑颖，陆瑛，陈松. 镍铬和含钛镍铬烤瓷合金的耐腐蚀性能研究[J]. 国际口腔医学杂志, 2009, 36(2): 152-152～155.

SUN Ping, FENG Jian-ying, LU Ying, CHEN Song. Corrosion resistance of Ni-Cr and Ni-Cr-Ti alloy in artificial saliva

[J]. Inter J Stomatol, 2009, 36(2): 152-152～155.

参考文献

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed

[1]	田陶然,张扬根,黄鑫琪,李龙飚,张心曦,朱卓立. 两种镍基口腔修复合金在漱口水中镍离子析出的比较[J]. 国际口腔医学杂志, 2016, 43(3): 278-282.
[2]	赵耀刘嘉俊综述孟玉坤审校. 牙科合金腐蚀行为的研究进展[J]. 国际口腔医学杂志, 2011, 38(3): 339-342.
[3]	褚凤清综述王国平审校. 牙科金属与合金腐蚀研究方法的进展[J]. 国际口腔医学杂志, 2010, 37(02): 189-189～191,195.
[4]	万书健,苏剑生,. 牙科合金引起不良反应的机制[J]. 国际口腔医学杂志, 2006, 33(05): 396-397.
[5]	曹艳兰,朱松. 牙科合金电偶腐蚀的研究进展[J]. 国际口腔医学杂志, 2005, 32(03): 216-218.
[6]	孙佳凝赵云凤高宁. 牙科合金材料的生物相容性及影响合金离子析出的因素[J]. 国际口腔医学杂志, 2003, 30(03): 212-214.
[7]	曹洪喜. 牙科金属与合金材料的腐蚀性能研究[J]. 国际口腔医学杂志, 2000, 27(02): -.