The research on the bond durability between self -adhesive cements and zirconia ceramic

Jing Ye, Meng Xiangfeng   

  1. Dept. of Prosthodontics, Nanjing Stomatological Hospital, School of Stomatology, Nanjing University,Nanjing 210008, China
  • Received:2012-12-31 Revised:2013-03-01 Online:2013-05-01 Published:2013-05-01

RichHTML

2

PDF (PC)

566

Abstract:

Objective To compare the bond durability of five self-adhesive resin cements to polished and sandblasted zirconia ceramic. Methods Zirconia ceramic samples were sintered and polished. Half of polished ceramic samples were sandblasted with 50 μm alumina particles. The roughness of polished and sandblasted zirconia ceramic surface was measured by 3D-laser scanning microscope. The polished and sandblasted ceramic samples were bonded to composite cylinders with either Biscem（BC）, G-Cem（GC）, RelyX U100（RU）, Multilink Speed（MS） or Maxcem （MC）. The samples divided into two subgroups to receive respectively shear test after 0 and 10 000 time thermal cycles. The data were analyzed by one-way ANOVA test and independent sample t test. Results Air abrasion significantly increased Ra of zirconia ceramic surface（P＜0.001）. Thermocycling decreased significantly the bond strengths of all test groups（P＜0.001）, in which polished specimens bonded with MS had significantly higher bond strength than those bonded with either BC, GC, RU, or MC（P＜0.001）, and air abrasion significantly increased the bond strength of BC, GC, RU and MC, whereas the bond strength of MS was not significantly affected by air abrasion. Conclusion The bond durability of different self-adhesive resin cements to zirconia ceramic has significant differences, and their bond durability was not completely influenced by air abrasion of ceramic surface.

Key words: zirconia ceramic, self-adhesive resin cement, bond strength, bond durability, polishing, sandblasting


TrendMD: 
[1] Ding Jingyu,Tian Zilu,Wang Huimin,Zhu Xuanyan,Yang Yubin,Zhu Song. Advancement of immediate dentin sealing [J]. Int J Stomatol, 2022, 49(1): 121-124.
[2] Li Min,Hua Chengge,Jiang Li. Research progress on new technology for improving adhesion properties of zirconia ceramics [J]. Int J Stomatol, 2021, 48(4): 485-490.
[3] Xin Tan,Haiyang Yu. Application of simulated pulpal pressure in dentine-bonding research [J]. Inter J Stomatol, 2018, 45(6): 723-727.
[4] Ding Hong, Chen Jifen, Wu Jianyong. Influence of different adhesive materials on the shear bond strength of metal brackets to porcelain surface [J]. Inter J Stomatol, 2017, 44(4): 430-432.
[5] Zhang Yarong, Liu Yang, Zhang Ling, Yu Haiyang. Quantitative analysis of the load tolerance of maxillary incisors with ceramic-laminated veneers for various incisal margin preparations [J]. Inter J Stomatol, 2017, 44(3): 301-303.
[6] Yao Chenmin, Zhou Liqun, Huang Cui.. Selection of tooth-colored restorative material for worn anterior teeth [J]. Inter J Stomatol, 2017, 44(3): 363-367.
[7] Ma Zhiling1, Liu Jie2. Effects of different surface treatments on the bonding strength of titanium and resin [J]. Inter J Stomatol, 2017, 44(1): 45-49.
[8] Yuan Xiaohui, Liu Jie.. Research progress on the effect of micro-arc oxidation on the bonding strength between pure titanium and porcelain [J]. Inter J Stomatol, 2016, 43(6): 695-699.
[9] Du Qiao, Niu Guangliang. Surface roughening zirconia and modification [J]. Inter J Stomatol, 2015, 42(1): 97-101.
[10] Sun Changjuan, Guan Hongyu, Han Lu. Clinical effects of an in-office desensitizing polishing paste containing arginine and calcium carbonate on root-dentin hypersensitivity after subgingival scaling with ultrasonic instruments [J]. Inter J Stomatol, 2014, 41(6): 663-666.
[11] Chen Chunxiu, Wen Xuejin.. Nursing cooperation for computer aided design and computer aided manufacturing of zirconia ceramic restoration system [J]. Inter J Stomatol, 2014, 41(2): 140-142.
[12] Gao Yu1, Wu Zhan’ao1, Feng Weizhong1, Ding Yan1, Zhang Deyun2, Jiang Tao1.. Effect of silicate solution in different concentrations on bonding strength of porcelain and pure titanium by liquid-phase deposition technology [J]. Inter J Stomatol, 2013, 40(4): 440-443.
[13] Lin Yihua1, Song Xiaomeng2, Zhang Wei3. Study of bonding property among 3 kinds of resin-reinforced glass ionomer and zirconia ceramics [J]. Inter J Stomatol, 2013, 40(3): 305-308.
[14] Weng Jiahua, Mai Lixiang, Wang Dawei.. Effect of tooth bleaching on the bond strength of orthodontic brackets [J]. Inter J Stomatol, 2013, 40(1): 105-108.
[15] Zhang Zhenliang, Fu Baiping.. Factors in testing the micro-tensile bond strength [J]. Inter J Stomatol, 2012, 39(5): 620-623.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[2] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[3] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[4] . [J]. Foreign Med Sci: Stomatol, 1999, 26(06): .
[5] . [J]. Foreign Med Sci: Stomatol, 1999, 26(05): .
[6] . [J]. Foreign Med Sci: Stomatol, 1999, 26(05): .
[7] . [J]. Foreign Med Sci: Stomatol, 1999, 26(04): .
[8] . [J]. Foreign Med Sci: Stomatol, 1999, 26(04): .
[9] . [J]. Foreign Med Sci: Stomatol, 2004, 31(02): 126 -128 .
[10] . [J]. Inter J Stomatol, 2008, 35(S1): .