国际口腔医学杂志

国际口腔医学杂志 ›› 2013, Vol. 40 ›› Issue (3): 305-308.doi: 10.7518/gjkq.2013.03.007

• 论著 • 上一篇    下一篇

3种树脂加强型玻璃离子与氧化锆陶瓷粘接性能的研究

林艺华1 宋晓萌2 张玮3   

  1. 1.浙江省象山县中医医院口腔科宁波315700；2.江苏省口腔医院口腔颌面外科， 南京医科大学口腔医学研究所；3.特诊科， 南京医科大学口腔医学研究所南京210029
  • 收稿日期:2012-07-23 修回日期:2013-01-29 出版日期:2013-05-01 发布日期:2013-05-01
  • 通讯作者: 张玮，Tel：025-85031817
  • 作者简介:林艺华（1977—），女，福建人，主治医师，学士
  • 基金资助:

    江苏高校优势学科建设工程基金资助项目（PADR2011-137）；南京医科大学科技发展基金资助面上项目（2010NJMU110）

Study of bonding property among 3 kinds of resin-reinforced glass ionomer and zirconia ceramics

Lin Yihua1, Song Xiaomeng2, Zhang Wei3   

  1. 1. Dept. of Stomatology, The Chinese Medicine Hospital of Xiangshan in Zhejiang Province, Ningbo 315700, China; 2. Dept. of Oral and Maxillofacial Surgery, Stomatological Hospital of Jiangsu Province, Institute of Stomatology of Nanjing Medical University, Nanjing 210029, China; 3. Dept. of Oral Special Consultation, Stomatological Hospital of Jiangsu Province, Institute of Stomatology of Nanjing Medical University, Nanjing 210029, China
  • Received:2012-07-23 Revised:2013-01-29 Online:2013-05-01 Published:2013-05-01

RichHTML

4

PDF (PC)

814

被引次数

10

摘要：

目的 探讨3种树脂加强型玻璃离子用于口腔科氧化锆陶瓷的粘接效果。方法 将烧结成型的氧化锆陶瓷片分为3组，每组20片，分别采用3种树脂加强型玻璃离子粘接剂与喷砂后的氧化锆陶瓷片粘接，在水浴24 h和冷热循环5 000次后测试其粘接剪切强度，数据用SPSS 11.5软件加以统计分析，粘接断面及剖面用扫描电子显微镜观察。结果 3种粘接剂与氧化锆陶瓷的粘接剪切强度分别为：（15.1±3.2）、（16.1±4.0）、（18.6±3.4）MPa（水浴24 h后），（5.1±2.1）、（7.5±2.9）、（8.7±2.6）MPa（冷热循环5 000次后）。冷热循环后各组的粘接剪切强度均有明显下降（P<0.05）。结论 树脂加强型玻璃离子粘接剂可以与氧化锆陶瓷产生良好的初期粘接强度，但效果不能持久。

关键词: 树脂加强型玻璃离子, 氧化锆陶瓷, 粘接剪切强度, 粘接持久性

Abstract:

Objective To study the bonding efficiency of zirconia ceramics with 3 kinds of resin-reinforced glass ionomer. Methods Blocks of sintered zirconia ceramics were cut and randomly divided into 3 groups with 20 slices each. They were treated with sandblasting and bonded with 3 kinds of resin-reinforced glass ionomer respectively. After preserved in distilled-water for 24 hours and aged by thermocycling 5 000 times, the shear bond strength of these specimens was tested and data were analyzed by SPSS 11.5 system for windows. The bonding face was observed by scanning electron microscope. Results The shear bond strength of the ceramic and 3 kinds of resin-reinforced glass ionomer was （15.1±3.2）, （16.1±4.0）, （18.6±3.4）MPa（after preserved in distilled-water for 24 hours） respectively, and decreased greatly to （5.1±2.1）, （7.5±2.9）, （8.7±2.6）MPa（after thermocycling 5 000 times）. There was obvious statistical difference before and after thermocycling（P<0.05）. Conclusion Resin-reinforced glass ionomer can get good initial bond strength with zirconia ceramics, but the bonding durability is poor.

Key words: resin-reinforced glass ionomer, zirconia ceramics, shear bond strength, bonding durability

[1] 黎敏,华成舸,蒋丽. 提高氧化锆陶瓷粘接性能新技术的研究进展[J]. 国际口腔医学杂志, 2021, 48(4): 485-490.
[2] 张雅蓉, 刘洋, 张玲, 于海洋. 不同切端设计的上前牙瓷贴面受载能力的定量研究[J]. 国际口腔医学杂志, 2017, 44(3): 301-303.
[3] 姚陈敏, 周丽群, 黄翠. 前牙磨耗牙色修复材料的选择[J]. 国际口腔医学杂志, 2017, 44(3): 363-367.
[4] 景页 孟翔峰. 自粘接树脂水门汀与二氧化锆陶瓷间粘接耐久性的研究[J]. 国际口腔医学杂志, 2013, 40(3): 301-304.
[5] 刘峰. 全瓷修复材料和方法的分化[J]. 国际口腔医学杂志, 2011, 38(4): 373-377.
[6] 谢彩虹1综述 刘新强2审校. 树脂加强型玻璃离子正畸粘接剂的研究进展[J]. 国际口腔医学杂志, 2008, 35(5): 596-596～.
[7] 金恩龙综述 焦艳军审校. 氧化锆陶瓷在口腔医学领域中的应用[J]. 国际口腔医学杂志, 2007, 34(01): 62-62～64.
[8] 卫晓霞,杨四维. 树脂加强型玻璃离子水门汀性能的研究现状[J]. 国际口腔医学杂志, 2005, 32(06): 423-425.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] 张京剧. 青年期至中年期颅面复合体变化的头影测量研究[J]. 国际口腔医学杂志, 1999, 26(06): .
[2] 刘玲. 镍铬合金中铍对可铸造性和陶瓷金属结合力的影响[J]. 国际口腔医学杂志, 1999, 26(06): .
[3] 王昆润. 在种植体上制作固定义齿以后下颌骨密度的动态变化[J]. 国际口腔医学杂志, 1999, 26(06): .
[4] 王昆润. 重型颌面部炎症死亡和康复病例的实验室检查指标比较[J]. 国际口腔医学杂志, 1999, 26(06): .
[5] 逄键梁. 两例外胚层发育不良儿童骨内植入种植体后牙槽骨生长情况[J]. 国际口腔医学杂志, 1999, 26(05): .
[6] 温秀杰. 氟化物对牙本质脱矿抑制作用的体外实验研究[J]. 国际口腔医学杂志, 1999, 26(05): .
[7] 杨春惠. 耳颞神经在颞颌关节周围的分布[J]. 国际口腔医学杂志, 1999, 26(04): .
[8] 王昆润. 牙周炎加重期应选用何种抗生素[J]. 国际口腔医学杂志, 1999, 26(04): .
[9] 杨儒壮 孙宏晨 欧阳喈. 纳米级高分子支架材料在组织工程中的研究进展[J]. 国际口腔医学杂志, 2004, 31(02): 126 -128 .
[10] 严超然,李龙江. 肿瘤靶向药物载体系统的研究进展[J]. 国际口腔医学杂志, 2008, 35(S1): .